FINISHES

# 1 -Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required.
# 2D -Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process. # 2B -Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D.
#BA-Bright annealed cold rolled and bright annealed
#CBA-Course bright annealed cold rolled matte finish and bright anneal
#2 -Cold Rolled
# 2BA-Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part. Polished -Various grit finish for specific polish finished requirements.
Not all finishes are available for all alloys - Contact Ulbrich Sales for more information.
WIRE FINISHES
XC - Extra clean bright annealed or bright annealed and cold rolled Grease - Ultra-bright finish (for decorative applications) Soap - Soap is not removed from tempered wire to act as a lubricant. *Contact Ulbrich Wire for custom wire finishes.
COLD FORMING
Type 436 is readily drawn and formed. Its drawing characteristics are similar to those of low carbon steel, although it is stronger in the annealed condition and will require stronger tooling and increased power. It is also adaptable to most hot-forming operations. It does have a slightly tendency to "rope" during forming, but it is minimized by the addition of colombium.