4mm thick stainless steel plate 420 446 steel sheet

Advantage

Heat Resistance
Grade 420 stainless steels have a scaling resistance at temperatures of up to 650°C. However, temperatures above standard tempering temperature are not suitable for this grade.
Back to Top
Machining
Grade 420 steels can be easily machined in their annealed state, but they are difficult to machine having a hardness greater than 30HRC. One of the most readily available machined alternatives is the free-machining grade 416 steels.
Back to Top
Welding
The martensitic class of stainless steels has limited weldability due to its hardenability. Special consideration is required to avoid cold cracking by preheating to 550°F (260°C). Post-weld heat treatment should be considered to achieve required properties. This particular alloy is generally considered to have poorer weldability than the most common alloy of this stainless class, Type 410. A major difference is higher carbon content for this alloy which requires both preheat and post-weld heat treatment. When a weld filler is needed, AWS E/ER 420, 410 NiMo and 309L are most often specified. Type 420 is well known in reference literature and more information can be obtained in this way.

Product parameters