Feature of 410 Stainless Steel Coil

Corrosion Resistance: 410 stainless steel exhibits resistance to a variety of environments including hot gases, steam, food, mild acids, alkalis, fresh water, and dry air. Optimal corrosion and heat resistance are achieved through hardening, although it's noteworthy that 410 exhibits less corrosion resistance compared to austenitic and 17% chromium ferritic stainless steels. A smooth surface enhances its corrosion resistance capabilities.

Heat Resistance: This grade offers commendable scaling resistance up to 650°C, with a caveat that mechanical properties may degrade in the 400 to 580°C range.

Heat Treating 410 stainless steel:

• Annealing: Full annealing can be done in the 815 to 900°C range, with slow furnace cooling and air-cooling.
• Hardening: Achievable at 925 to 1010°C followed by air and oil quenching. Heavy sections require oil quenching, with subsequent tempering to improve mechanical properties and hardness, avoiding the 400 to 580°C range to prevent loss of mechanical properties.

Welding: Weldable by all standard methods; however, pre-heating at 150 to 260°C and post-weld annealing are advised to prevent cracking. Using grade 410 welding rods is recommended, with grade 309 filler rods as an alternative for more ductile joints.

Machining: Machinability is optimal in annealed or highly tempered states. Hardened conditions above 30HRC diminish machinability, with grade 416 being a preferable option for easier machining.

Product Parameters

Product Name	410 Stainless Steel Coil
Type	Steel Coil
Thickness	2.5mm-10.0mm
Length	2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc.
Width	610mm-2000mm
Standard	ASTM, AISI, JIS, GB, DIN, EN, etc.
Surface	BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc.
Scope of Application	Widely used in high temperature and electrical industry, medical equipment construction, chemical, food industry, agriculture and ship parts, food and beverage packaging, Kitchen supplies, trains, airplanes, conveyor belts, vehicles, bolts, nuts, springs and screens, etc.
Certificate	ISO, SGS, BV, etc.
Production Technology	Hot Rolling, Cold Rolling
Edge Processing	Edging, Trimming

410 Stainless Steel Standards Comparison

STS	USA	UNS	CHINA	EURONORM		RUSSIA	SWEDISH	JAPANESE
GRADE	AISI/ASTM	NO	GB	NO	NAME	GOST	SS	JIS
410	410	S41000	0Cr13	1.4006	X12Cr13	30Х13	2302	SUS 410

410 Stainless Steel Chemical Composition

Grade	Standard	Chemical Composition(%)
		C	Si	Mn	P	S	Cr	Ni
410	ASTM A240	≤0.08~0.15	≤1.00	≤1.00	≤0.040	≤0.030	11.50~13.50	≤0.75

410 Stainless Steel Mechanical Properties

Grade	AISI/ASTM	Tensile Test			Hardness Test
		0.2% Y.S(Mpa)	T.S(Mpa)	Elongation(%)	Hardness	HRB
410	ASTM A240	≥275	≥485	≥20	Annealed	96

Why Choose Us

Behind the growth and success of Kuaima Steel is years of hard work and dedication in the steel industry and meeting customers' needs on time. Advanced technology, standard products, certified quality standards and the bestcustomer service make Kuiama Steel a true leader in the global market.

Service field

Every industry has its unique set of material specifications and needs. That’s why you can count on the exceptional experience and industry knowledge of the professionals at Kuaima Steel - Meeting the Exact Needs of Every Industry That Uses steel.

• 
  

  Machinery manufacturing industry
• 

  Power Ceneration
• 
  

  Oil & Gas
• 

  Manufacturing
• 

  Construction
• 
  

  Ship building
• 

  Automobile manufacturing
• 
  

  Pipe Fabrication